Fluoride-free synthesis of anodic TiO2 nanotube layers: a promising environmentally friendly method for efficient photocatalyst

Hanif M. B., Thirunavukkarasu G. K., Liapun V., Makarov H., Gregor M., Roch T., Plecenik T., Rauf S., Hensel K., Sihor M., Monfort O., Motola M.
Nanoscale 14 (32), 11703, 7 pp (2022)

download  

Abstrakt:

TiO2 nanotube (TNT) layers are generally prepared in fluoride-based electrolytes via electrochemical anodization that relies on the field-assisted dissolution of Ti metal forming nanoporous/nanotubular structures. However, the usage of fluoride ions is considered hazardous to the environment. Therefore, we present an environmentally friendly synthesis and application of TNT layers prepared in fluoride-free nitratebased
electrolytes. A well-defined nanotubular structure with thickness up to 1.5 μm and an inner tube diameter of ∼55 nm was obtained within 5 min using aqueous X(NO3)Y electrolytes (X = Na+, K+, Sr2+, Ag+). For the first time, we show the photocatalytic performance (using a model organic pollutant), HO• radical production, and thorough characterization of TNT layers prepared in such electrolytes. The highest degradation efficiency (k = 0.0113 min−1) and HO• radical production rate were obtained using TNT layers prepared in AgNO3 (Ag-NT). The intrinsic properties of Ag-NT such as the valence band maximum of ∼2.9 eV, surface roughness of ∼6 nm, and suitable morphological features and crystal structure were obtained. These results have the potential to pave the way for a more environmentally friendly synthesis of anodic TNT layers in the future using the next generation of fluoride-free nitrate-based electrolytes.